1. Nchịkọta nke ígwè cryogenic
1) The teknuzu chọrọ maka ala-okpomọkụ ígwè n'ozuzu: ike zuru ezu na zuru ezu ike na a ala-okpomọkụ gburugburu ebe obibi, ezigbo ịgbado ọkụ arụmọrụ, nhazi arụmọrụ na corrosion iguzogide, wdg N'etiti ha, ala okpomọkụ siri ike, ya bụ, ikike. iji gbochie ihe omume na mgbasawanye nke mgbaji na-agbaji na obere okpomọkụ bụ ihe kacha mkpa. Ya mere, mba na-edobekarị uru siri ike mmetụta ụfọdụ na okpomọkụ kacha ala.
2) N'ime ihe ndị dị na nchara dị ala, a na-ekwenyekarị na ihe ndị dị ka carbon, silicon, phosphorus, sulfur, na nitrogen na-eme ka ike dị ala na-eme ka okpomọkụ dị ala, na phosphorus bụ nke kachasị njọ, ya mere n'oge okpomọkụ dephosphorization kwesịrị ịdị. rụrụ n'oge agbaze. Ihe ndị dị ka manganese na nickel nwere ike imeziwanye ike okpomọkụ dị ala. Maka mmụba 1% ọ bụla na ọdịnaya nickel, enwere ike ibelata okpomọkụ mgbanwe dị egwu site na ihe dịka 20 Celsius.
3) Usoro ọgwụgwọ okpomọkụ na-enwe mmetụta dị mkpa na nhazi metallographic na nha ọka nke obere okpomọkụ, nke na-emetụtakwa obere okpomọkụ siri ike nke ígwè. Ka emechara ọgwụgwọ na iwe ọkụ, a na-emeziwanye ike ike dị ala.
4) Dị ka ụzọ dị iche iche na-ekpo ọkụ na-ekpo ọkụ si dị, a na-ekewa nchara na-ekpo ọkụ n'ime ihe nkedo na nchara. Dị ka ihe dị iche nke mejupụtara na metallographic Ọdịdị, ala okpomọkụ ígwè nwere ike kewara n'ime: obere alloy ígwè, 6% nickel ígwè, 9% nickel ígwè, chromium-manganese ma ọ bụ chromium-manganese-nickel austenitic ígwè na chromium-nickel austenitic igwe anaghị agba nchara. chere. A na-ejikarị ígwè dị ala na-eme ihe n'ụdị okpomọkụ dị ihe dị ka -100 Celsius maka imepụta ngwa nju oyi, ngwa njem, ụlọ nchekwa vinyl na ngwa petrochemical. Na United States, United Kingdom, Japan na mba ndị ọzọ, a na-eji 9% nickel steel mee ihe na ụlọ okpomọkụ dị ala na 196 Celsius, dị ka tankị nchekwa maka nchekwa na njem nke biogas na methane, ngwá ọrụ maka ịchekwa oxygen mmiri mmiri. , na imepụta ikuku oxygen na mmiri mmiri nitrogen. Igwe anaghị agba nchara Austenitic bụ ezigbo ihe nhazi dị ala dị ala. Ọ nwere ịdị ike dị ala nke ọma, arụmọrụ ịgbado ọkụ dị mma, yana njikwa ọkụ dị ala. A na-eji ya n'ọtụtụ ebe na mpaghara okpomọkụ dị ala, dị ka ụgbọ mmiri na-ebufe na tankị nchekwa maka hydrogen mmiri na mmiri oxygen. Otú ọ dị, n'ihi na ọ nwere ọtụtụ chromium na nickel, ọ dị oke ọnụ.
2. Nchịkọta nke obere okpomọkụ ígwè ịgbado ọkụ ewu
Mgbe ị na-ahọrọ usoro ịgbado ọkụ na ọnọdụ ihe owuwu nke ígwè dị ala, ihe na-elekwasị anya na nsogbu ahụ bụ n'akụkụ abụọ ndị a: igbochi nbibi nke obere okpomọkụ siri ike nke nkwonkwo welded na igbochi ihe omume nke ịgbado ọkụ.
1) Nhazi bevel
The uzo ụdị nke ala-okpomọkụ ígwè welded nkwonkwo adịghị iche na ụkpụrụ na nke nkịtị carbon ígwè, ala alloy ígwè ma ọ bụ igwe anaghị agba nchara, na ike na-emeso dị ka ọ dị na mbụ. Mana maka 9Ni Gang, oghere oghere nke uzo ahụ ga-akacha mma ọ bụghị ihe na-erughị ogo 70, na ihu na-adịghị mma bụ ọkachamma ọ bụghị ihe na-erughị 3mm.
Enwere ike iji ọkụ oxyacetylene bee nchara niile dị ala. Ọ bụ naanị na ịcha ọsọ bụ ubé nwayọọ nwayọọ mgbe gas ọnwụ 9Ni ígwè karịa mgbe gas ọnwụ nkịtị carbon structural ígwè. Ọ bụrụ na ọkpụrụkpụ nke ígwè ahụ gafere 100mm, a ga-eme ka ọ dị ọkụ ruo 150-200 Celsius C tupu egbutu gas, ma ọ bụghị ihe karịrị 200 ° C.
Mbelata gas enweghị mmetụta ọjọọ na mpaghara ọkụ ịgbado ọkụ na-emetụta. Otú ọ dị, n'ihi njide onwe onye nke ígwè nwere nickel, elu nke ịkpụ ga-esiwanye ike. Iji hụ na arụmọrụ na-eju afọ nke nkwonkwo welded, ọ ka mma iji igwe na-egweri na-egweri elu nke elu nke ịkpụ dị ọcha tupu ịgbado ọkụ.
Enwere ike iji gouging arc ma ọ bụrụ na a ga-ewepụ bead weld ma ọ bụ ọla ala n'oge a na-arụ ọrụ ịgbado ọkụ. Otú ọ dị, a ka kwesịrị ịchacha elu nke notch ahụ dị ọcha tupu etinyeghachi ya.
Oxyacetylene ire ọkụ ekwesịghị iji gouging n'ihi ihe ize ndụ nke ikpo oke ígwè.
2) Nhọrọ nke usoro ịgbado ọkụ
Ụzọ ịgbado ọkụ a na-ahụkarị maka igwe na-ekpo ọkụ na-agụnye ịgbado ọkụ arc, ịgbado ọkụ n'okpuru mmiri, na ịgbado ọkụ argon arc a wụrụ awụ.
Arc ịgbado ọkụ bụ usoro ịgbado ọkụ a na-ejikarị eme ihe maka nchara dị ala, yana enwere ike ịgbado ya n'ọnọdụ ịgbado ọkụ dị iche iche. Ntinye ọkụ ịgbado ọkụ bụ ihe dịka 18-30KJ / cm. Ọ bụrụ na a na-eji electrode dị ala-hydrogen mee ihe, enwere ike ịnweta nkwonkwo welded zuru oke na-eju afọ. Ọ bụghị nanị na n'ibu Njirimara dị mma, ma notch siri ike dịkwa nnọọ mma. Tụkwasị na nke ahụ, igwe ịgbado ọkụ arc dị mfe ma dị ọnụ ala, na ntinye ego akụrụngwa dị ntakịrị, ọ naghị emetụta ọnọdụ na ntụziaka. uru dị ka njedebe.
Ntinye ọkụ nke ịgbado ọkụ n'okpuru mmiri nke ígwè dị ala dị ala bụ ihe dịka 10-22KJ / cm. N'ihi ngwá ọrụ ya dị mfe, ịrụ ọrụ ịgbado ọkụ dị elu na ọrụ dị mma, a na-eji ya eme ihe. Otú ọ dị, n'ihi mmetụta na-ekpo ọkụ na-ekpo ọkụ nke mgbanwe ahụ, a ga-ebelata ọnụ ọgụgụ dị jụụ, ya mere enwere ọchịchọ dị ukwuu nke ịmepụta ọkụ ọkụ. Na mgbakwunye, adịghị ọcha na Si nwere ike na-abanyekarị nchara weld site na mgbawa ahụ, nke ga-agbakwu ume nke a. Ya mere, mgbe ị na-eji submerged arc ịgbado ọkụ, ntị na nhọrọ nke ịgbado ọkụ waya na flux na-arụ ọrụ nke ọma.
Ngwunye ịgbado ọkụ nke CO2 gas na-echebe welding nwere obere siri ike, ya mere a naghị eji ha na mgbado ọkụ dị ala.
Tungsten argon arc welding (TIG welding) na-ejikarị aka eme ya, yana ntinye ọkụ ịgbado ọkụ ya bụ naanị 9-15KJ/cm. Ya mere, ọ bụ ezie na nkwonkwo welded nwere ihe zuru oke na-eju afọ, ha adịghị mma mgbe ọkpụkpụ ígwè karịrị 12mm.
MIG ịgbado ọkụ bụ nke a na-ejikarị akpaka ma ọ bụ ọkara akpaaka ịgbado ọkụ usoro na obere okpomọkụ ígwè ịgbado ọkụ. Ntinye ọkụ ịgbado ọkụ ya bụ 23-40KJ / cm. Dị ka usoro mbufe droplet si dị, enwere ike kewaa ya n'ime ụdị atọ: usoro nnyefe nke mkpirikpi (ntụgharị okpomọkụ dị ala), usoro mbufe jet (ntinye okpomọkụ dị elu) na usoro mbufe pulse jet (ntụnye ọkụ kacha elu). Mgbanwe mgbanwe oge dị mkpirikpi MIG ịgbado ọkụ nwere nsogbu nke enweghị ntinye zuru oke, na ntụpọ nke ngwakọta adịghị mma nwere ike ime. Nsogbu ndị yiri ya dị na mgbanwe MIG ndị ọzọ, mana n'ọkwa dị iche. Iji mee ka arc ahụ gbasie ike iji nweta ntinye afọ ojuju, ọtụtụ pasent ruo iri iri nke CO2 ma ọ bụ O2 nwere ike ịbanye n'ime argon dị ọcha dị ka gas na-echebe. A ga-ekpebi pasentị kwesịrị ekwesị site na ịnwale maka otu ígwè a na-agbado.
3) Nhọrọ nke ihe ịgbado ọkụ
Ihe eji agbado ọkụ (gụnyere mkpanaka ịgbado ọkụ, waya ịgbado ọkụ na flux, wdg) kwesịrị dabere na usoro ịgbado ọkụ ejiri. Ụdị nkwonkwo na ụdị uzo na njirimara ndị ọzọ dị mkpa ịhọrọ. Maka nchara dị ala, ihe kachasị mkpa ị ga-aṅa ntị bụ ime ka metal weld nwere obere okpomọkụ siri ike iji kwekọọ na metal ntọala, ma belata ọdịnaya nke hydrogen na-agbasasị n'ime ya.
Mgbado ọkụ Xinfa nwere ezigbo mma yana ịdịte aka siri ike, maka nkọwa, biko lelee:https://www.xinfatools.com/welding-cutting/
(1) Aluminom deoxidized ígwè
Aluminom deoxidized ígwè bụ ọkwa nchara nke na-enwe mmetụta nke ukwuu na mmetụta nke nju oyi mgbe ịgbado ọkụ. Ọtụtụ n'ime electrodes eji na akwụkwọ ntuziaka arc welding nke aluminum deoxidized steel bụ Si-Mn obere-hydrogen electrodes ma ọ bụ 1.5% Ni na 2.0% Ni electrodes.
Iji belata ntinye ọkụ ịgbado ọkụ, aluminum deoxidized ígwè n'ozuzu nanị nakweere multi-layer welding na mkpa electrodes nke ≤¢3 ~ 3.2mm, nke mere na nke abụọ okpomọkụ okirikiri nke elu oyi akwa nke weld nwere ike iji nụchaa ọka.
Mmetụta siri ike nke igwe weld welded na Si-Mn usoro electrode ga-ebelata nke ọma na 50 ℃ na mmụba nke ntinye ọkụ. Dịka ọmụmaatụ, mgbe ntinye ọkụ na-abawanye site na 18KJ / cm ruo 30KJ / cm, ike ga-efunahụ karịa 60%. 1.5%Ni series na 2.5%Ni series welding electrodes adịghị emetụ n'ahụ nke a, ya mere ọ kacha mma ịhọrọ ụdị electrode a maka ịgbado ọkụ.
Ịgbado ọkụ n'okpuru mmiri bụ usoro ịgbado ọkụ akpaka na-ejikarị maka aluminum deoxidized steel. Waya ịgbado ọkụ a na-eji n'ime mmiri ịgbado ọkụ n'okpuru mmiri bụ ọkachamma ụdị nwere 1.5 ~ 3.5% nickel na 0.5 ~ 1.0% molybdenum.
Dị ka akwụkwọ akụkọ si kwuo, na 2.5% Ni-0.8% Cr-0.5% Mo ma ọ bụ 2% Ni waya ịgbado ọkụ, dakọtara na kwesịrị ekwesị flux, nkezi Charpy siri ike uru nke weld metal na -55°C nwere ike iru 56-70J (5.7). 7.1Kgf.m). Ọbụlagodi mgbe ejiri 0.5% Mo welding waya na manganese alloy basic flux, ọ bụrụhaala na a na-achịkwa ntinye ọkụ n'okpuru 26KJ/cm, a ka nwere ike imepụta ígwè weld nwere ν∑-55=55J (5.6Kgf.m).
Mgbe ị na-ahọrọ ntugharị, ekwesịrị itinye nlebara anya na ndakọrịta nke Si na Mn na igwe weld. Nnwale akaebe. Ọdịnaya Si na Mn dị iche iche na igwe weld ga-agbanwe uru ịdị ike Charpy nke ukwuu. Ọdịnaya Si na Mn nwere uru siri ike kachasị mma bụ 0.1 ~ 0.2% Si na 0.7 ~ 1.1%Mn. Mgbe ị na-ahọrọ waya ịgbado ọkụ na mara nke a mgbe soldering.
Tungsten argon arc welding na metal argon arc welding bụ obere eji na aluminum deoxidized ígwè. Enwere ike iji wires ịgbado ọkụ ndị dị n'elu maka ịgbado ọkụ arc okpuru mmiri maka ịgbado ọkụ argon arc.
(2) 2.5Ni ígwè na 3.5Ni
Igwe ịgbado ọkụ nke submerged arc ma ọ bụ MIG ịgbado ọkụ nke 2.5Ni ígwè na 3.5Ni ígwè nwere ike n'ozuzu welded na otu ịgbado ọkụ waya dị ka isi ihe. Mana dị ka usoro Wilkinson (5) na-egosi, Mn bụ ihe mgbochi na-ekpo ọkụ na-ekpo ọkụ maka nchara dị ala dị ala. Idobe ọdịnaya manganese na igwe weld na ihe dịka 1.2% bara ezigbo uru iji gbochie mgbawa ọkụ dị ka mgbawa arc crater. Ekwesịrị iburu nke a n'uche mgbe ị na-ahọrọ ngwakọta nke waya ịgbado ọkụ na flux.
3.5Ni ígwè na-achọ ka a na-ewe iwe na embrittled, ya mere, mgbe ọgwụgwọ okpomọkụ nke post-weld (dịka ọmụmaatụ, 620 ° C × 1 hour, mgbe ahụ ọkụ ọkụ) iji kpochapụ nrụgide fọdụrụnụ, ν∑-100 ga-adaba ngwa ngwa site na 3.8 Kgf.m ka 2.1Kgf.m enweghị ike imezu ihe achọrọ. Igwe weld nke kpụrụ site na ịgbado ọkụ na 4.5%Ni-0.2%Mo usoro ịgbado ọkụ waya nwere nnọọ nta ọchịchọ nke iwe embrittlement. Iji waya ịgbado ọkụ a nwere ike zere ihe isi ike ndị dị n'elu.
(3) 9Ni ígwè
9Ni nchara na-abụkarị okpomọkụ na-agwọ ya site n'imenyụ na iwe ọkụ ma ọ bụ ugboro abụọ na-eme ka ọ dị mma ma na-ewe iwe ka ọ dịkwuo ọkụ ọkụ dị ala. Ma ígwè weld nke ígwè a enweghị ike ịgwọ okpomọkụ dị ka n'elu. Ya mere, ọ na-esiri ike ịnweta ígwè weld nke nwere obere okpomọkụ siri ike tụnyere nke metal ala ma ọ bụrụ na ejiri ígwè na-emepụta ihe ịgbado ọkụ. Ka ọ dị ugbu a, a na-ejikarị ihe ịgbado ọkụ nke nickel eme ihe. Ngwongwo ndị a na-echekwa site na ihe ndị dị otú ahụ na-agbado ọkụ ga-abụ kpamkpam austenitic. Ọ bụ ezie na ọ nwere ihe ọghọm nke ike dị ala karịa 9Ni steel base material na ọnụ ahịa dị oke ọnụ, mgbaji na-agbaji abụghịzi nsogbu siri ike maka ya.
Site n'elu, ọ nwere ike mara na n'ihi na weld metal bụ kpamkpam austenitic, ala okpomọkụ siri ike nke weld metal eji maka ịgbado ọkụ na electrodes na wires bụ kpamkpam tụnyere nke isi metal, ma tensile ike na mkpụrụ ebe bụ. ala karịa isi metal. Nchara nwere nickel na-eme ka onwe ya sie ike, ya mere ọtụtụ electrodes na wires na-aṅa ntị na ịmachi ọdịnaya carbon iji nweta ezigbo weldability.
Mo bụ ihe dị mkpa na-ewusi ike na ihe ịgbado ọkụ, ebe Nb, Ta, Ti na W bụ ihe dị mkpa na-eme ka ike sie ike, bụ nke enyerela nlebara anya zuru oke na nhọrọ nke ihe ịgbado ọkụ.
Mgbe a na-eji otu waya ịgbado ọkụ ahụ maka ịgbado ọkụ, ike na ike nke igwe weld nke welding arc submerged dị njọ karịa nke MIG ịgbado ọkụ, nke nwere ike bute ya site na mbelata nke weld jụrụ oyi na enwere ike ịbanye na adịghị ọcha ma ọ bụ Si. site na ntughari nke.
3. A333-GR6 obere okpomọkụ ígwè anwụrụ ịgbado ọkụ
1) Weldability analysis nke A333-GR6 ígwè
A333-GR6 ígwè bụ nke obere okpomọkụ ígwè, kacha nta ọrụ okpomọkụ bụ -70 ℃, na ọ na-emekarị na-ọnọ na normalized ma ọ bụ normalized na tempered ala. A333-GR6 ígwè nwere obere carbon ọdịnaya, ya mere ike siri ike na oyi na-atụ cracking bụ dịtụ obere, ihe onwunwe nwere ezi ike na plasticity, ọ dịghị mfe n'ozuzu na-emepụta hardening na mgbape ntụpọ, na nwere ezi weldability. ER80S-Ni1 argon arc welding waya nwere ike iji W707Ni electrode, jiri argon-electric nkwonkwo ịgbado ọkụ, ma ọ bụ na-eji ER80S-Ni1 argon arc welding waya, na-eji zuru argon arc ịgbado ọkụ iji hụ na ezi ike nke welded nkwonkwo. The ika nke argon arc ịgbado ọkụ waya na electrode nwekwara ike họrọ ngwaahịa na otu arụmọrụ, ma ha nwere ike na-eji naanị na nkwenye nke onye nwe.
2) Usoro ịgbado ọkụ
Maka usoro usoro ịgbado ọkụ zuru ezu, biko rụtụ aka na akwụkwọ ntuziaka usoro ịgbado ọkụ ma ọ bụ WPS. N'oge ịgbado ọkụ, I-ụdị butt nkwonkwo na zuru argon arc ịgbado ọkụ na-nakweere maka ọkpọkọ na a dayameta na-erughị 76.2 mm; maka ọkpọkọ nke nwere dayameta karịa 76.2 mm, a na-eme oghere ndị dị ka V, na usoro nke argon-electric combing welding na argon arc priming na multi-layer filling na-eji ma ọ bụ Usoro nke zuru ezu argon arc ịgbado ọkụ. Usoro a kapịrị ọnụ bụ ịhọrọ usoro ịgbado ọkụ kwekọrọ dịka ọdịiche dị na dayameta ọkpọkọ na ọkpụrụkpụ mgbidi ọkpọkọ na WPS nke onye nwe ya kwadoro.
3) Usoro ọgwụgwọ okpomọkụ
(1) Ịkpọ ọkụ tupu ịgbado ọkụ
Mgbe ọnọdụ okpomọkụ dị n'okpuru 5 Celsius C, ọ dị mkpa ka welded ahụ kpoo ọkụ, na ikpo ọkụ na-ekpo ọkụ bụ 100-150 ° C; ihe nkedo preheating bụ 100 mm n'akụkụ abụọ nke weld; a na-eji ọkụ oxyacetylene na-ekpo ọkụ (ọkụ na-anọpụ iche), a na-atụkwa okpomọkụ ahụ Pen na-atụle okpomọkụ dị n'ebe dị anya nke 50-100 mm site na etiti nke weld, a na-ekesakwa ihe nlele okpomọkụ nke ọma ka ọ dịkwuo mma ịchịkwa okpomọkụ. .
(2) Ngwọta okpomọkụ mgbe weld gasịrị
Iji kwalite ọkwa siri ike nke ígwè dị ala, ihe ndị a na-ejikarị eme ihe emenyụla ma kpasuo ya iwe. Ngwọta okpomọkụ na-adịghị mma mgbe e mesịrị weld na-emekarị ka arụmọrụ ya dị ala na-akawanye njọ, nke kwesịrị ịkwụ ụgwọ zuru oke. Ya mere, ewezuga ọnọdụ nke nnukwu welding ọkpụrụkpụ ma ọ bụ ọnọdụ njide siri ike, a naghị emekarị ọgwụgwọ okpomọkụ mgbe weld maka ígwè dị ala. Dịka ọmụmaatụ, ịgbado ọkụ nke pipeline LPG ọhụrụ na CSPC anaghị achọ ọgwụgwọ okpomọkụ mgbe weld gasịrị. Ọ bụrụ na a chọrọ n'ezie ọgwụgwọ okpomọkụ post-weld na ụfọdụ oru ngo, okpomọkụ ọnụego, mgbe niile okpomọkụ oge na obi jụrụ ọnụego post-weld okpomọkụ ọgwụgwọ ga-n'ezie dị ka ndị na-esonụ ụkpụrụ:
Mgbe okpomọkụ na-ebili n'elu 400 ℃, ọkụ ọkụ ekwesịghị gafere 205 × 25 / δ ℃ / h, na ekwesịghị gafere 330 ℃ / h. Oge okpomọkụ mgbe niile kwesịrị ịbụ 1 hour kwa 25 mm ọkpụrụkpụ mgbidi, na ọ bụghị ihe na-erughị 15 nkeji. N'ime oge okpomọkụ na-adịgide adịgide, ọdịiche dị n'etiti okpomọkụ kachasị elu na nke dị ala kwesịrị ịdị ala karịa 65 ℃.
Mgbe okpomọkụ na-adị mgbe niile, ọnyà jụrụ oyi ekwesịghị ịbụ ihe karịrị 65 × 25 / δ ℃ / h, na ekwesịghị ịbụ ihe karịrị 260 ℃ / h. A na-ahapụ ikuku oyi n'okpuru 400 ℃. TS-1 ụdị ọgwụgwọ okpomọkụ nke kọmputa na-achịkwa.
4) Akpachara anya
(1) Kpoo ọkụ dị ka ụkpụrụ si dị, ma na-achịkwa okpomọkụ nke interlayer, na-achịkwa okpomọkụ nke interlayer na 100-200 ℃. A ga-ejigide eriri ịgbado ọkụ ọ bụla n'otu oge, ma ọ bụrụ na ọ kwụsịtụrụ, a ga-ewere usoro jụrụ oyi ngwa ngwa.
(2) A machibidoro elu nke weldment ka ọ ghara ịcha ya site na arc. Ekwesịrị ka ejupụta oghere arc na ntụpọ ndị ahụ ga-eji wiil egweri mee ihe mgbe a na-emechi arc ahụ. Njikọ dị n'etiti ọkwa nke ịgbado ọkụ multi-layer kwesịrị ịkwanye.
(3) Jikwaa ike ahịrị nke ọma, were obere ọkụ ugbu a, voltaji dị ala na ịgbado ọkụ ngwa ngwa. Ogologo ịgbado ọkụ nke electrode W707Ni ọ bụla nwere dayameta nke 3.2 mm ga-abụrịrị 8 cm.
(4) A ghaghị ịnakwere ọnọdụ ọrụ nke obere arc na ọ dịghị swing.
(5) The zuru penetration usoro ga-nakweere, na ọ ga-rụrụ n'ụzọ siri ike dabere na chọrọ nke ịgbado ọkụ usoro nkọwapụta na ịgbado ọkụ usoro kaadị.
(6) Nkwado nke weld bụ 0 ~ 2mm, na obosara nke akụkụ ọ bụla nke weld bụ ≤ 2mm.
(7) Enwere ike ịme nnwale na-adịghị emebi emebi ma ọ dịkarịa ala awa 24 mgbe nyocha anya weld ruru eru. Ọkụ ọkpọ ọkpọ ọkpọkọ ga-adị n'okpuru JB 4730-94.
(8) “Ụgbọ mmiri nrụgide: Nnwale na-adịghị emebi emebi nke ụgbọ mmiri nrụgide”, Klas II tozuru oke.
(9) Weld mmezi kwesịrị rụrụ tupu post-weld okpomọkụ ọgwụgwọ. Ọ bụrụ na nrụzi dị mkpa mgbe ọgwụgwọ okpomọkụ gasịrị, a ga-ekpocha weld ahụ ọzọ mgbe emezichara ya.
(10) Ọ bụrụ na geometric akụkụ nke weld elu karịa ọkọlọtọ, egweri na-ekwe, na ọkpụrụkpụ mgbe egweri agaghị abụ ihe na-erughị imewe chọrọ.
(11) Maka ntụpọ ịgbado ọkụ n'ozuzu, a na-ahapụ kacha nke nrụzi abụọ. Ọ bụrụ na nrụzi abụọ ahụ erughị eru, a ga-ebipụ weld ahụ ma gbanye ya ọzọ dịka usoro ịgbado ọkụ zuru oke.